S-Plastics Verton M3000C resin is an anti-static compound based on Polypropylene. Characteristics are Clean Compound System.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 18 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 689 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 760 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 24 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 860 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 24 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 690 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1180 | MPa | ISO 527 |
| Flexural Stress | 38 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1960 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 75 | J/m | ASTM D 256 |
| Multiaxial Impact | 25 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 29 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 74 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 49 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 1.28E-04 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 1.31E-04 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 75 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 49 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 0.93 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.16 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1 - 2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 2 | % | ASTM D 955 |
| Density | 0.93 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.16 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.2E+01 | Ohm | ASTM D 257 |
| Source GMD, last updated:2009/01/13 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 70 - 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 190 - 200 | °C |
| Front - Zone 3 Temperature | 200 - 210 | °C |
| Middle - Zone 2 Temperature | 195 - 205 | °C |
| Rear - Zone 1 Temperature | 180 - 195 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/01/13 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton M3000C.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|