S-Plastics Verton ITF2B resin is a compound based on Nylon 6/12 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this
material include: Thermally Conductive.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 79 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9980 | MPa | ASTM D 638 |
| Flexural Stress | 144 | MPa | ASTM D 790 |
| Flexural Modulus | 9250 | MPa | ASTM D 790 |
| Tensile Stress, break | 80 | MPa | ISO 527 |
| Tensile Strain, break | 2.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10200 | MPa | ISO 527 |
| Flexural Stress | 144 | MPa | ISO 178 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 421 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 8 | J | ASTM D 3763 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 28 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 167 | °C | ASTM D 648 |
| Thermal Conductivity | 1.1 | W/m-°C | ASTM E 1530 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 158 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.9 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.5 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.89 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.45 | % | ISO 294 |
| Moisture Absorption (23°C / 50% RH) | 0.12 | % | ISO 62 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12 - 0.2 | % |
| Melt Temperature | 270 - 275 | °C |
| Front - Zone 3 Temperature | 270 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 270 | °C |
| Rear - Zone 1 Temperature | 255 - 265 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton ITF2B.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|