S-Plastics Geloy CR7010 resin is ASA copolymer for sheet extrusion applications. High impact, weatherable capstock.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 42 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 35 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1930 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 60 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1930 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 91 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 480 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 106 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 24 | J | ASTM D 3763 |
| Instrumented Impact Total Energy, -30°C | 16 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 102 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 90 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 76 | °C | ASTM D 648 |
| HDT, 1.82 MPa, annealed | 97 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 96 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 85 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.08E-04 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 50 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 50 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.06 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.5 | % | S-Plastics Method |
| Melt Flow Rate, 220°C/10.0 kgf | 3.7 | g/10 min | ASTM D 1238 |
| Melt Flow Rate, 260°C/5.0 kgf | 3.5 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Gloss, untextured, 60 degrees | 95 | - | ASTM D 523 |
| ELECTRICAL | Value | Unit | Standard |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.49 | mm | UL 94 |
| UV-light, water exposure/immersion | F2 | - | UL 746C |
| Source GMD, last updated:06/29/1998 | |||
| • Barrel temperatures should be banked TO 150°C (300°F) | ||
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Minimum Moisture Content | 0.04 | % |
| Melt Temperature | 220 - 245 | °C |
| Barrel - Zone 1 Temperature | 180 - 225 | °C |
| Barrel - Zone 2 Temperature | 190 - 230 | °C |
| Barrel - Zone 3 Temperature | 205 - 240 | °C |
| Barrel - Zone 4 Temperature | 210 - 245 | °C |
| Adapter Temperature | 210 - 245 | °C |
| Die Temperature | 210 - 245 | °C |
| Roll Stack Temp - Top | 70 - 100 | °C |
| Roll Stack Temp - Middle | 70 - 95 | °C |
| Roll Stack Temp - Bottom | 65 - 90 | °C |
| Source GMD, last updated:06/29/1998 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Geloy CR7010.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|