S-Plastics Valox VX7024 resin is a 12% mineral filled PBT injection moulding resin with excellent mechanical properties.
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 35 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 5 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 13 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3200 | MPa | ISO 178 |
| Hardness, H358/30 | 130 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.15E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.15E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 187 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 150 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 60 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 1 - 2 | % | S-Plastics Method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 27 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 4.E+16 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | 7.3E+17 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.1 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0016 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.0175 | - | IEC 60250 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Source GMD, last updated:06/15/1999 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 285 | °C |
| Nozzle Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 255 - 280 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 110 | °C |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox VX7024.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|