S-Plastics Valox VIC4350 resin is
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 106 | MPa | S-Plastics - Japan Method |
| Tensile Strain, break | 5 - 5 | % | S-Plastics - Japan Method |
| Flexural Stress | 169 | MPa | ASTM D 790 |
| Flexural Modulus | 8330 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 137 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 206 | °C | ASTM D 648 |
| CTE, -30°C to 30°C | 3.E-05 - 3.E-05 | 1/°C | TMA |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.55 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.07 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.1 - 0.3 | % | S-Plastics Method |
| Mold Shrinkage, flow, 6.4 mm | 0.7 - 0.9 | % | S-Plastics Method |
| Source GMD, last updated:02/03/2000 |
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 265 | °C |
| Nozzle Temperature | 245 - 260 | °C |
| Front - Zone 3 Temperature | 250 - 265 | °C |
| Middle - Zone 2 Temperature | 245 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 255 | °C |
| Mold Temperature | 65 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.025 - 0.038 | mm |
| Source GMD, last updated:10/13/2004 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox VIC4350.pdf |
|