S-Plastics Valox K4530 resin is 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 103 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 103 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 3550 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 150 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4640 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 400 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 218 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 193 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.41 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 0.9 | % S-Plastics Method | |
| Mold Shrinkage, xflow, 3.2 mm | 1 - 1.2 | % S-Plastics Method | |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 82 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % ASTM D 638 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4520 | MPa | ASTM D 790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 9.7 | % ASTM D 790 | |
| Instrumented Impact, Total Energy, 23°C | 6 | J | ASTM D 3763 |
| PROPERTIES AFTER 1008 HOURS AT 125?C | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 98 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % ASTM D 638 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4820 | MPa | ASTM D 790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 7 | % ASTM D 790 | |
| Instrumented Impact, Total Energy, 23°C | 5 | J | ASTM D 3763 |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 89 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.3 | % ASTM D 638 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5100 | MPa | ASTM D 790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 6 | % ASTM D 790 | |
| Instrumented Impact, Total Energy, 23°C | 4 | J | ASTM D 3763 |
| PROPERTIES AFTER 1008 HOURS AT 155?C | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 4812 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 97.2 | % ASTM D 638 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 0 | MPa | ASTM D 790 |
| Flexural Strain, 1.3 mm/min, 50 mm span | 3.8 | % | ASTM D 790 |
| Source GMD, last updated:03/25/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 60 - 75 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 250 - 265 | °C |
| Nozzle Temperature | 245 - 260 | °C |
| Front - Zone 3 Temperature | 250 - 265 | °C |
| Middle - Zone 2 Temperature | 245 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 255 | °C |
| Mold Temperature | 65 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.025 - 0.038 | mm |
| Source GMD, last updated:03/25/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox K4530.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|