S-Plastics Valox V8090 resin is 50% Glass Fiber Reinforced PBT-PET resin
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 175 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 175 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 17500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 255 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 16000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 1.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 210 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 206 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.76 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.16 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 7 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:05/21/2008 | |||
|