S-Plastic Valox 467 resin Is 30% Glass Reinforced Flame Retarded Impact Modified PBT Injection Moulding

100KG
MOQ
*USD
Price
S-Plastic Valox 467 resin Is 30% Glass Reinforced Flame Retarded Impact Modified PBT Injection Moulding
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 8
UL Recognized, 94HB Flame Class Rating (3): 1.5
Highlight:

Flame Retarded

Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Valox
Certification: COA/ICP Test/Rohs/MSDS
Model Number: 467
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Valox 467 resin is 30% glass reinforced, flame retarded, impact modified PBT injection moulding resin. This grade is a 420SE0 with improvedductility.


Property

MECHANICAL Value Unit Standard
Tensile Stress, break, 5 mm/min 115 MPa ISO 527
Tensile Strain, break, 5 mm/min 3 % ISO 527
Tensile Modulus, 1 mm/min 8500 MPa ISO 527
Flexural Stress, break, 2 mm/min 175 MPa ISO 178
Flexural Modulus, 2 mm/min 7600 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*4 +23°C 60 kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C 65 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 7 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 6 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 8 kJ/m² ISO 179/1eA
Charpy Impact, notched, 23°C 12 kJ/m² ISO 179/2C
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm 7 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm 50 kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm 50 kJ/m² ISO 179/1eU
Izod Reverse Impact, notched 80*10*4,23°C 45 kJ/m² ISO 180/1C
THERMAL Value Unit Standard
Thermal Conductivity 0.19 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 1.6E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 1.2E-04 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate A/50 213 °C ISO 306
Vicat Softening Temp, Rate B/50 155 °C ISO 306
Vicat Softening Temp, Rate B/120 170 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 205 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 165 °C ISO 75/Ae
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/impact 120 °C UL 746B
Relative Temp Index, Mech w/o impact 140 °C UL 746B
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) 0.1 - 0.3 % S-Plastics Method
Mold Shrinkage on Tensile Bar, xflow (2) 0.4 - 0.7 % S-Plastics Method
Density 1.56 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.25 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.07 % ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg 8 cm³/10 min ISO 1133
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 0.8 mm 26 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm 24 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm 16 kV/mm IEC 60243-1
Relative Permittivity, 50/60 Hz 3.6 - IEC 60250
Relative Permittivity, 1 MHz 3.4 - IEC 60250
Dissipation Factor, 50/60 Hz 0.003 - IEC 60250
Dissipation Factor, 1 MHz 0.01 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) 1.5 mm UL 94
Glow Wire Flammability Index 960°C, passes at 1 mm IEC 60695-2-12
Oxygen Index (LOI) 28 % ISO 4589
Source GMD, last updated:10/15/1992    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 110 - 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250 - 270 °C
Nozzle Temperature 240 - 260 °C
Front - Zone 3 Temperature 245 - 265 °C
Middle - Zone 2 Temperature 240 - 255 °C
Rear - Zone 1 Temperature 230 - 245 °C
Hopper Temperature 40 - 60 °C
Mold Temperature 40 - 100 °C
Source GMD, last updated:10/15/1992  

 

 

For more information please download the datasheet

S-Plastic Valox 467 resin Is 30% Glass Reinforced Flame Retarded Impact Modified PBT Injection Moulding 0  SS-Plastics Valox 467.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Valox 467 resin Is 30% Glass Reinforced Flame Retarded Impact Modified PBT Injection Moulding 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastic Valox 467 resin Is 30% Glass Reinforced Flame Retarded Impact Modified PBT Injection Moulding 2

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)