S-Plastics Valox FXV310SK resin is an unreinforced PBT injection moulding Visualfx* resin with high flow characteristics and containing a metal sparkle.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 17 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 20 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2700 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 89 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 9 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 58 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2750 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2750 | MPa | ISO 178 |
| Hardness, H358/30 | 85 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 117 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 56 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 3 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 55 | °C | ASTM D 648 |
| CTE, -20°C to 150°C, xflow | 1.3E-04 | 1/°C | ASTM E 831 |
| CTE, 0°C to 100°C, flow | 1.3E-04 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.16 | W/m-°C | ISO 8302 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 187 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 160 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 55 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 1.9 - 2.4 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/2.16 kgf | 27.5 | g/10 min | ASTM D 1238 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.34 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.02 | - | IEC 60250 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.47 | mm | UL 94 by GE |
| UL Compliant, 94HB Flame Class Rating 2nd value (3)(4) | 3.12 | mm | UL 94 by GE |
| Oxygen Index (LOI) | 20 | % | ISO 4589 |
| Source GMD, last updated:11/02/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:11/02/2006 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox FXV310SK.pdf |
|