S-Plastics Valox 牌号EXVX1302 resin is Non Halogen Flame retardant based on environmentally sustainable iQ PBT resin
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 170 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Source GMD, last updated:09/14/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:09/14/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1302.pdf |
|