S-Plastics Valox EXVX1300 resin is a 15% glass reinforced injection molding PET grade for food packging applications
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 120 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 230 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.2 - 0.4 | % | S-Plastics Method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.12 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 12 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| Source GMD, last updated:06/25/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 90 - 120 | °C |
| Source GMD, last updated:06/25/2008 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1300.pdf |
|