S-Plastics Valox 3607U resin is a UV-stabilized, flame retardant, injection moulding PBT resin, offering excellent weatherability resistance. Applications:powerplugs.
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2050 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2050 | MPa | ISO 178 |
| Hardness, H358/30 | 91 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 116 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 1.05E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.1E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 160 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 125 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 130 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 110 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 80 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 1 - 1.8 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.9 - 1.8 | % | S-Plastics Method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.5 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Melt Flow Rate, 250°C/5.0 kg | 16 | g/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 14 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0028 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.0129 | - | IEC 60250 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-1 Flame Class Rating (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 850°C, passes at | 1.6 | mm | IEC 60695-2-12 |
| Source GMD, last updated:04/07/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:04/07/1999 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox 3607U.pdf |
|