S-Plastics Valox 327resin is Unreinforced, impact modified polyester, high ductility and good processability.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 200 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 151 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 54 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.29 | - | ASTM D 792 |
| Specific Volume | 0.77 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.08 | % | ASTM D 570 |
| Mold Shrinkage, flow, 0.75-2.3 mm | 1.4 - 1.8 | % | S-Plastics Method |
| Mold Shrinkage, flow, 2.3-4.6 mm | 1.7 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 1.4 - 1.8 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 2.3-4.6 mm | 1.7 - 2.2 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 0.8 mm | 15.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 MHz | 2.9 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 |
| Source GMD, last updated:01/05/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 260 | °C |
| Nozzle Temperature | 240 - 255 | °C |
| Front - Zone 3 Temperature | 245 - 260 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 250 | °C |
| Mold Temperature | 50 - 75 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.013 - 0.025 | mm |
| Source GMD, last updated:01/05/2000 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox 327.pdf |
|