S-Plastics Xylex EXXX0051 resin is PC+Polyester alloy. Transparent with with excellent optical quality. USA/Europe Food contact.
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min | 63 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min | 6.3 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 135 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min | 2140 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D 790 |
Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5.8 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 133 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 92 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2250 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C | 854 | J/m | ASTM D 256 |
Instrumented Impact Total Energy, 23°C | 70 | J | ASTM D 3763 |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -10°C | 6 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 | 126 | °C | ASTM D 1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 119 | °C | ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D 648 |
CTE, -40°C to 40°C, flow | 1.04E-04 | 1/°C | ASTM E 831 |
CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
CTE, 23°C to 60°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/120 | 126 | °C | ISO 306 |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 106 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
Melt Flow Rate, 265°C/2.16kg | 12 | g/10 min | ASTM D 1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 265°C/2.16 kg | 11 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Light Transmission | 88 | % | ASTM D 1003 |
Haze | 2 | % | ASTM D 1003 |
Source GMD, last updated:08/22/2005 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 65 - 80 | °C |
Drying Time | 3 - 5 | hrs |
Drying Time (Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 250 - 270 | °C |
Nozzle Temperature | 250 - 270 | °C |
Front - Zone 3 Temperature | 250 - 270 | °C |
Middle - Zone 2 Temperature | 245 - 270 | °C |
Rear - Zone 1 Temperature | 245 - 260 | °C |
Mold Temperature | 45 - 60 | °C |
Back Pressure | 0.1 - 0.5 | MPa |
Screw Speed | 20 - 100 | rpm |
Shot to Cylinder Size | 40 - 80 | % |
Vent Depth | 0.013 - 0.02 | mm |
Source GMD, last updated:08/22/2005 |
Other related products we recommend:
For more information please download the datasheet |
|
![]() |
S-Plastics Xylex EXXX0051.pdf |