S-Plastics Xylex EXXX0013 resin is PC+Polyester alloy. Unreinforced, transparent, chemically resistant, specially designed for lens applications.
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -10°C | 8 | kJ/m² | ISO 180/1A |
THERMAL | Value | Unit | Standard |
Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
CTE, 23°C to 60°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/120 | 124 | °C | ISO 306 |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 108 | °C | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Density | 1.18 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 265°C/2.16 kg | 9 | cm³/10 min | ISO 1133 |
OPTICAL | Value | Unit | Standard |
Haze | 1.6 | % | ASTM D 1003 |
Source GMD, last updated:10/01/2002 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 80 - 95 | °C |
Drying Time | 3 - 5 | hrs |
Drying Time (Cumulative) | 8 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 250 - 270 | °C |
Nozzle Temperature | 250 - 270 | °C |
Front - Zone 3 Temperature | 250 - 270 | °C |
Middle - Zone 2 Temperature | 245 - 265 | °C |
Rear - Zone 1 Temperature | 240 - 250 | °C |
Mold Temperature | 45 - 60 | °C |
Back Pressure | 0.2 - 0.5 | MPa |
Screw Speed | 20 - 100 | rpm |
Shot to Cylinder Size | 40 - 80 | % |
Vent Depth | 0.013 - 0.02 | mm |
Source GMD, last updated:10/01/2002 |
Other related products we recommend:
For more information please download the datasheet |
|
![]() |
S-Plastics Xylex EXXX0013.pdf |