| Tensile Stress, yld, Type I, 50 mm/min |
63 |
MPa |
ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min |
6 |
% |
ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min |
>70 |
% |
ASTM D638 |
| Tensile Modulus, 50 mm/min |
2350 |
MPa |
ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span |
90 |
MPa |
ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span |
2300 |
MPa |
ASTM D790 |
| Hardness, Rockwell R |
120 |
- |
ASTM D785 |
| Tensile Stress, yield, 50 mm/min |
63 |
MPa |
ISO 527 |
| Tensile Strain, yield, 50 mm/min |
6 |
% |
ISO 527 |
| Tensile Strain, break, 50 mm/min |
>70 |
% |
ISO 527 |
| Tensile Modulus, 1 mm/min |
2350 |
MPa |
ISO 527 |
| Flexural Stress, yield, 2 mm/min |
90 |
MPa |
ISO 178 |
| Flexural Modulus, 2 mm/min |
2300 |
MPa |
ISO 178 |
| Hardness, Rockwell R |
120 |
- |
ISO 2039-2 |
| IMPACT |
|
|
|
| Izod Impact, unnotched, 23°C |
NB |
J/m |
ASTM D4812 |
| Izod Impact, notched, 23°C |
900 |
J/m |
ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C |
65 |
J |
ASTM D3763 |
| Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C |
NB |
kJ/m² |
ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C |
70 |
kJ/m² |
ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C |
12 |
kJ/m² |
ISO 180/1A |
| THERMAL |
|
|
|
| Vicat Softening Temp, Rate B/50 |
144 |
°C |
ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm |
138 |
°C |
ASTM D648 |
| HDT, 1.82 MPa, 3.2 mm |
127 |
°C |
ASTM D648 |
| CTE, -40°C to 95°C, flow |
7.00E-05 |
1/°C |
ASTM E831 |
| Thermal Conductivity |
0.2 |
W/m-°C |
ASTM C177 |
| Thermal Conductivity |
0.2 |
W/m-°C |
ISO 8302 |
| CTE, 23°C to 80°C, flow |
7.00E-05 |
1/°C |
ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C |
Passes |
- |
IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 |
144 |
°C |
ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
138 |
°C |
ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
127 |
°C |
ISO 75/Af |
| PHYSICAL |
|
|
|
| Specific Gravity |
1.2 |
- |
ASTM D792 |
| Water Absorption, (23°C/Saturated) |
0.35 |
% |
ASTM D570 |
| Mold Shrinkage on Tensile Bar, flow |
0.5-0.7 |
% |
S-Plastics method |
| Mold Shrinkage, flow, 3.2 mm |
0.5-0.7 |
% |
S-Plastics method |
| Melt Flow Rate, 300°C/1.2 kgf |
7 |
g/10 min |
ASTM D1238 |
| Density |
1.2 |
g/cm³ |
ISO 1183 |
| Water Absorption, (23°C/saturated) |
0.35 |
% |
ISO 62-1 |
| Melt Volume Rate, MVR at 300°C/1.2 kg |
6 |
cm³/10 min |
ISO 1133 |
| OPTICAL |
|
|
|
| Light Transmission, 2.54 mm |
88-90 |
% |
ASTM D1003 |
| Haze, 2.54 mm |
<0.8 |
% |
ASTM D1003 |
| Refractive Index |
1.586 |
- |
ASTM D542 |
| Refractive Index |
1.586 |
- |
ISO 489 |
| ELECTRICAL |
|
|
|
| Volume Resistivity |
>1.E+15 |
Ω.cm |
ASTM D257 |
| Dielectric Strength, 1.6 mm |
27 |
kV/mm |
ASTM D149 |
| Relative Permittivity, 60 Hz |
3 |
- |
ASTM D150 |
| Relative Permittivity, 1 MHz |
3 |
- |
ASTM D150 |
| Dissipation Factor, 60 Hz |
0.001 |
- |
ASTM D150 |
| Dissipation Factor, 1 MHz |
0.01 |
- |
ASTM D150 |
| Volume Resistivity |
>1.E+15 |
Ω.cm |
IEC 60093 |
| Dielectric Strength, 1.6 mm |
27 |
kV/mm |
IEC 60243-1 |
| Relative Permittivity, 60 Hz |
3 |
- |
IEC 60250 |
| Relative Permittivity, 1 MHz |
3 |
- |
IEC 60250 |
| Dissipation Factor, 60 Hz |
0.001 |
- |
IEC 60250 |
| Dissipation Factor, 1 MHz |
0.01 |
- |
IEC 60250 |
| FLAME CHARACTERISTICS |
|
|
|
| UL Yellow Card Link |
E207780-101295396 |
- |
- |
| UL Recognized, 94V-2 Flame Class Rating |
1.6 |
mm |
UL 94 |