S-Plastics Verton W3000 resin is a compound based on Polybutylene Terephalate resin containing Anti-Static. Added features of this material
include: Antistat.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 41 | MPa | ASTM D 638 |
| Tensile Stress, break | 40 | MPa | ASTM D 638 |
| Tensile Strain, yield | 8.2 | % | ASTM D 638 |
| Tensile Strain, break | 14.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1580 | MPa | ASTM D 638 |
| Flexural Stress | 59 | MPa | ASTM D 790 |
| Flexural Modulus | 1720 | MPa | ASTM D 790 |
| Tensile Stress, yield | 37 | MPa | ISO 527 |
| Tensile Stress, break | 37 | MPa | ISO 527 |
| Tensile Strain, yield | 10.9 | % | ISO 527 |
| Tensile Strain, break | 12.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1630 | MPa | ISO 527 |
| Flexural Stress | 58 | MPa | ISO 178 |
| Flexural Modulus | 1640 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1254 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 32 | J | ASTM D 3763 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 137 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 46 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.27 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.65 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1.7 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 2 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 1.74 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.99 | % | ISO 294 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.09 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+09 - 1.E+11 | Ohm | ASTM D 257 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 220 - 230 | °C |
| Front - Zone 3 Temperature | 220 - 230 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 205 - 215 | °C |
| Mold Temperature | 10 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton W3000.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|