S-Plastics Geloy XTWE280 resin is Weatherble ASA profile extrusion grade
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 46 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 33 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 13 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2700 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 78 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2500 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 37 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 31 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2850 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 74 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 75 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 42 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 30 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 86 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 80 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 86 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 88 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 74 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.1 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.52 - 0.53 | % | S-Plastics Method |
| Melt Flow Rate, 200°C/3.8 kgf | 12 | g/10 min | ASTM D 1238 |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.26 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 11 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:05/31/2007 | |||
| Parameter | ||
| Profile Extrusion | Value | Unit |
| Drying Temperature | 85 - 95 | °C |
| Drying Time | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 190 - 210 | °C |
| Barrel - Zone 1 Temperature | 180 - 200 | °C |
| Barrel - Zone 2 Temperature | 180 - 200 | °C |
| Barrel - Zone 3 Temperature | 180 - 205 | °C |
| Barrel - Zone 4 Temperature | 180 - 205 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Adapter Temperature | 180 - 205 | °C |
| Die Temperature | 185 - 205 | °C |
| Calibrator Temperature | 50 - 70 | °C |
| Source GMD, last updated:05/31/2007 | ||
|