S-Plastics Geloy FXW740ME resin is specially designed as a caplayer for co-extrusion with CYCOLAC WP1. It demonstrates a superior UV stability and excellent melt strength.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 180 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 30 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 2.8 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 55 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 |
| Hardness, H358/30 | 72 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 97 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.21 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 90 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 95 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 75 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.7 | % | S-Plastics Method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.52 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 2 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/10 kg | 12 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1 | mm | UL 94 by GE |
| UL Compliant, 94HB Flame Class Rating 2nd value (3)(4) | 3 | mm | UL 94 by GE |
| Glow Wire Flammability Index 750°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 19 | % | ISO 4589 |
| Source GMD, last updated:09/21/2000 | |||
| Parameter | ||
| Profile Extrusion | Value | Unit |
| Drying Temperature | 85 - 95 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 210 - 240 | °C |
| Barrel - Zone 1 Temperature | 180 - 210 | °C |
| Barrel - Zone 2 Temperature | 190 - 220 | °C |
| Barrel - Zone 3 Temperature | 200 - 230 | °C |
| Barrel - Zone 4 Temperature | 200 - 230 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Adapter Temperature | 200 - 230 | °C |
| Die Temperature | 200 - 230 | °C |
| Calibrator Temperature | 50 - 70 | °C |
| Source GMD, last updated:09/21/2000 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Geloy FXW740ME.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|