S-Plastics Geloy EXGY0010 resin is a high heat resistant ASA+PC. It shows high impact retention, which can be positioned for various outdoor and indoor applications requiring superior heat aging properties and colour stability.Properties measured on a color containing 7% inorganic pigments
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 67 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 210 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2420 | MPa | ASTM D 638 |
| Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 5.2 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 130 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2290 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 81 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2140 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 380 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 53 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 23 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 134 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 136 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 114 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.6 | % | S-Plastics Method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.6 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 14 | cm³/10 min | ISO 1133 |
| OPTICAL | Value | Unit | Standard |
| Gloss, untextured, 60 degrees | 99 | - | ASTM D 523 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index, M | 450 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating 2nd value (3)(4) | 3 | mm | UL 94 by GE |
| Glow Wire Flammability Index 750°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Source GMD, last updated:08/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 100 - 110 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 290 | °C |
| Nozzle Temperature | 240 - 280 | °C |
| Front - Zone 3 Temperature | 250 - 290 | °C |
| Middle - Zone 2 Temperature | 250 - 290 | °C |
| Rear - Zone 1 Temperature | 230 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |
| Source GMD, last updated:08/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Geloy EXGY0010.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|