S-Plastics Geloy EXGY0009 resin is a general purpose ASA/PC injection moulding grade, available in various colors.Properties measured on color containing
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 35 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2370 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2210 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, -40°C to 40°C, flow | 9.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 108 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.1 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.8 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 10 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 280 | °C |
| Nozzle Temperature | 230 - 270 | °C |
| Front - Zone 3 Temperature | 240 - 280 | °C |
| Middle - Zone 2 Temperature | 230 - 270 | °C |
| Rear - Zone 1 Temperature | 220 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 50 - 80 | °C |
| Source GMD, last updated:08/02/2004 | ||