S-Plastics Stat-kon RE004 resin is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 219 | MPa | ASTM D 638 |
| Tensile Strain, break | 4.3 | % | ASTM D 638 |
| Flexural Stress | 312 | MPa | ASTM D 790 |
| Flexural Modulus | 12340 | MPa | ASTM D 790 |
| Tensile Stress, break | 233 | MPa | ISO 527 |
| Tensile Strain, break | 2.9 | % | ISO 527 |
| Flexural Stress | 337 | MPa | ISO 178 |
| Flexural Modulus | 14600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 523 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 54 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.25 | g/cm³ | ASTM D 792 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||