S-Plastics Stat-kon PX98038 resin is a compound based on PA6 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features
include : Flame Retardant, Electrically Conductive, Heat Stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 136 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 2 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 12200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 201 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 199 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3.9 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 9400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 8.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.3 | % | S-Plastics Method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+04 - 1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 3 | mm | UL 94 by GE |
| Source GMD, last updated:04/02/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 75 - 85 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.2 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 250 - 270 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 70 - 90 | °C |
| Source GMD, last updated:04/02/2008 |