S-Plastics Stat-kon PX09011 resin is a compound based on PA 6 resin containing Carbon Powder, Glass Fiber. Added features
include:Electrically Conductive, Easy Molding, Heat Stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 106 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.31 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+07 - 1.E+09 | Ohm | ASTM D 257 |
| Source GMD, last updated:2009/12/22 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 275 - 290 | °C |
| Middle - Zone 2 Temperature | 265 - 275 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/12/22 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon PX09011.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|