S-Plastics Stat-kon PX08019 resin is a compound based on PA 6 resin containing Glass Fiber, Carbon Fiber, Flame Retardant. Added features
include; Non-Halogen Flame Retardant, Electrically Conductive.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 160 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 230 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 11500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 207 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.2 - 0.4 | % | S-Plastics Method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+04 - 1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Source GMD, last updated:12/17/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 75 - 85 | °C |
| Drying Time | 4 - 6 | hrs |
| Melt Temperature | 250 - 270 | °C |
| Front - Zone 3 Temperature | 250 - 270 | °C |
| Middle - Zone 2 Temperature | 250 - 270 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Mold Temperature | 70 - 90 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:12/17/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon PX08019.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|