S-Plastics Stat-kon PE002Z resin is a compound based on Nylon 6 with Carbon Fiber. Characteristics: Extrusion Grade.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 32 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 210 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 121 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4070 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 59 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 10.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 870 | MPa | ISO 527 |
| Flexural Stress | 82 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2130 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1305 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 11 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 65 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 194 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 131 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 5.3E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 9.4E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 195 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.18 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.93 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1 - 2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D 955 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.93 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 7.E+00 - 9.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:2009/01/13 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 255 - 265 | °C |
| Front - Zone 3 Temperature | 250 - 260 | °C |
| Middle - Zone 2 Temperature | 250 - 260 | °C |
| Rear - Zone 1 Temperature | 245 - 255 | °C |
| Mold Temperature | 55 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/01/13 | ||
Other related products we recommend:
|