S-Plastics Stat-kon OX92182 resin is a compound based on PPS-Branched resin containing Glass Fiber, Carbon Fiber, Mineral. Added features
include : Electrically Conductive.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 145 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 17500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 200 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 16500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.1 | % | ISO 294 |
| Density | 1.62 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/26/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 315 - 320 | °C |
| Front - Zone 3 Temperature | 330 - 345 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 305 - 315 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/26/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon OX92182.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|