S-Plastics Stat-kon OE008 resin is a compound based on PPS-Linear resin containing Carbon Fiber. Added features include: Electically
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 178 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 30300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 253 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 251 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 25300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 5.E-06 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 3.9E-05 | 1/°C | ISO 11359-2 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.1 | % | S-Plastics Method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+03 | Ohm | ASTM D 257 |
| Source GMD, last updated:11/13/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 315 - 320 | °C |
| Front - Zone 3 Temperature | 330 - 345 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 305 - 315 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:11/13/2007 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon OE008.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|