S-Plastics Stat-kon OE006 resin is a compound based on PPS - Linear resin containing Carbon Fiber. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 186 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 23920 | MPa | ASTM D 638 |
| Flexural Stress | 282 | MPa | ASTM D 790 |
| Flexural Modulus | 21160 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 640 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 108 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.43 | g/cm³ | ASTM D 792 |
| Source GMD, last updated:2010/03/16 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 315 - 320 | °C |
| Front - Zone 3 Temperature | 330 - 345 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 305 - 315 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/03/16 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon OE006.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|