S-Plastics Stat-kon MX01739C resin is a compound based on Polypropylene containing Proprietary Fillers. Characteristics of this grade are:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 28 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 6930 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 41 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5580 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 25 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5240 | MPa | ISO 527 |
| Flexural Stress | 40 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5590 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 68 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 34 | J/m | ASTM D 256 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 15 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 134 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 94 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 1.7E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 7.74E+01 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 83 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.04 | - | ASTM D 792 |
| Density | 1.03 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.02 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.6 - 0.9 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 1 - 4 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.02 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 4.E+00 - 7.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:2009/09/02 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/09/02 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon MX01739C.pdf |
|