S-Plastics Stat-kon KX97157 resin is a compound based on Acetal resin containing Carbon. Added features include : Electrically Conductive,
Impact Modified.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 84 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13100 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 96 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 89 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 1.7 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 9600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 3.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.8E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.12 | % | S-Plastics Method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+03 | Ohm | ASTM D 257 |
| Source GMD, last updated:03/10/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 200 - 215 | °C |
| Front - Zone 3 Temperature | 210 - 220 | °C |
| Middle - Zone 2 Temperature | 195 - 205 | °C |
| Rear - Zone 1 Temperature | 175 - 190 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:03/10/2008 | ||