S-Plastics Stat-kon DX98477 resin is a compound based on Polycarbonate containing proprietary fillers. Characteristics of this grade are Statically
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 59 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 49 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 4.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 21.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2790 | MPa | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2890 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 46 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 21.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 |
| Flexural Stress | 89 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2720 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 2330 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 87 | J/m | ASTM D 256 |
| Multiaxial Impact | 34 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 45 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 234 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 142 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 133 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 6.7E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 6.6E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 142 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 132 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.25 | - | ASTM D 792 |
| Density | 1.25 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.16 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.8 - 1 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.8 - 1 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.24 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 2.E+00 - 6.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:2010/07/19 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/07/19 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DX98477.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|