S-Plastics Stat-kon DX04089C resin is a high modulus compound based on Polycarbonate resin containing Carbon Fiber. Added features of
this material include: Clean Compounding System. This grade is formerly known as Stat-Kon* PDX-D-04489 CCS
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 130 | MPa | ASTM D 638 |
| Tensile Stress, break | 111 | MPa | ASTM D 638 |
| Tensile Strain, yield | 2.2 | % | ASTM D 638 |
| Tensile Strain, break | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 16630 | MPa | ASTM D 638 |
| Flexural Stress | 206 | MPa | ASTM D 790 |
| Flexural Modulus | 15530 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 480 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 11 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 140 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.62E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 4.14E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.33 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+02 - 1.E+06 | Ohm | ASTM D 257 |
| Source GMD, last updated:04/01/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:04/01/2005 |
Other related products we recommend:
|
For more information please download the datesheet |
|
 |