S-Plastics Stat-kon DS0029 resin is a compound based on Polycarbonate resin containing Stainless Steel. Added features of this material
include: Electrically Conductive.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 57 | MPa | ASTM D 638 |
| Tensile Stress, break | 49 | MPa | ASTM D 638 |
| Tensile Stress, yld, Type I, 5 mm/min | 53 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 44 | MPa | ASTM D 638 |
| Tensile Strain, yield | 4.3 | % | ASTM D 638 |
| Tensile Strain, break | 7.8 | % | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 13.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D 638 |
| Flexural Stress | 96 | MPa | ASTM D 790 |
| Flexural Modulus | 2900 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 48 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2320 | MPa | ISO 527 |
| Flexural Stress | 76 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2230 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1600 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 93 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 15 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 88 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 133 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D 648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.29 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.65 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.73 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.21 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 3.E+00 - 6.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:01/03/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 95 - 120 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:01/03/2005 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DS0029.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|