S-Plastics Stat-kon DE0049F resin is a carbon fiber filled polycarbonate with flame retardant and superior molding characteristics.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 137 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 137 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 13420 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11550 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 134 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 134 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14970 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 166 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 166 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 11650 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 488 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 47 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 29 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 146 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 143 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.23E+00 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.79E+00 | 1/°C | ASTM E 831 |
| CTE, 23°C to 60°C, flow | 1.23E+00 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.79E+00 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 148 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 144 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.33 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.13 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.7 - 1 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.7 | % | ASTM D 955 |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.18 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+00 - 3.E+00 | Ohm | ASTM D 257 |
| Source GMD, last updated:03/26/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:03/26/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DE0049F.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|