Sabic Verton WV007S resin is a compound based on Polybutylene Terephalate resin containing Long Glass Fiber. Added features of this
material include: Heat Stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 145 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.4 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 14000 | MPa | ASTM D 638 |
| Flexural Stress | 213 | MPa | ASTM D 790 |
| Flexural Modulus | 10390 | MPa | ASTM D 790 |
| Tensile Stress, break | 141 | MPa | ISO 527 |
| Tensile Strain, break | 1.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13440 | MPa | ISO 527 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Flexural Modulus | 11240 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 694 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 277 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 11 | J | ASTM D 3763 |
| Multiaxial Impact | 9 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 27 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 222 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.48E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.62E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.4E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 231 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.59 | g/cm³ | ASTM D 792 |
| Source GMD, last updated:02/27/2007 | |||
For more information please download the datasheet | |
 | Sabic Verton WV007S.pdf |