S-Plastics Verton WV006 resin is a compound based on Polybutylene Terephalate resin containing Long Glass.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 187 | MPa | ISO 527 |
| Tensile Strain, break | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11570 | MPa | ISO 527 |
| Flexural Stress | 247 | MPa | ISO 178 |
| Flexural Modulus | 9780 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 36 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 225 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Source GMD, last updated:10/03/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 250 - 260 | °C |
| Front - Zone 3 Temperature | 250 - 260 | °C |
| Middle - Zone 2 Temperature | 240 - 250 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Mold Temperature | 65 - 120 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 70 | rpm |
| Source GMD, last updated:10/03/2004 | ||
For more information please download the datasheet | |
 | S-Plastics Verton WV006.pdf |