S-Plastics Verton UX06451 resin is a compound based on Polyphthalamide resin containing Long Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 274 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 19300 | MPa | ASTM D 638 |
| Tensile Stress, break | 275 | MPa | ISO 527 |
| Tensile Strain, break | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 19000 | MPa | ISO 527 |
| Flexural Stress | 375 | MPa | ISO 178 |
| Flexural Modulus | 17400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1495 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 411 | J/m | ASTM D 256 |
| Multiaxial Impact | 14 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 75 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, -40°C to 40°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 3.2E-05 | 1/°C | ISO 11359-2 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.63 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.3 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.06 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.2 | % | ISO 294 |
| Density | 1.63 | g/cm³ | ISO 1183 |
| Source GMD, last updated:01/02/2007 | |||
|
For more information please download the datasheet |
|
 |
S-Plastics Verton UX06451.pdf |
|