S-Plastics Verton UV00AS resin is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material
include: Heat Stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 257 | MPa | ASTM D 638 |
| Tensile Stress, break | 257 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1.8 | % | ASTM D 638 |
| Tensile Strain, break | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 19300 | MPa | ASTM D 638 |
| Flexural Stress | 386 | MPa | ASTM D 790 |
| Flexural Modulus | 17230 | MPa | ASTM D 790 |
| Tensile Stress, yield | 222 | MPa | ISO 527 |
| Tensile Stress, break | 222 | MPa | ISO 527 |
| Tensile Strain, yield | 1.4 | % | ISO 527 |
| Tensile Strain, break | 1.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 19220 | MPa | ISO 527 |
| Flexural Stress | 393 | MPa | ISO 178 |
| Flexural Modulus | 17000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1228 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 267 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 9 | J | ASTM D 3763 |
| Multiaxial Impact | 7 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 78 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 41 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 291 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 266 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.06E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.44E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 296 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 272 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.67 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.48 | % | ISO 294 |
| Density | 1.66 | g/cm³ | ISO 1183 |
| Source GMD, last updated:06/13/2007 | |||
|