S-Plastics Verton OX07411 resin is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 191 | MPa | ASTM D 638 |
| Tensile Stress, break | 191 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1.6 | % | ASTM D 638 |
| Tensile Strain, break | 1.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 15780 | MPa | ASTM D 638 |
| Flexural Stress | 267 | MPa | ASTM D 790 |
| Flexural Modulus | 16750 | MPa | ASTM D 790 |
| Tensile Stress, yield | 198 | MPa | ISO 527 |
| Tensile Stress, break | 198 | MPa | ISO 527 |
| Tensile Strain, yield | 1.8 | % | ISO 527 |
| Tensile Strain, break | 1.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14400 | MPa | ISO 527 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Flexural Modulus | 17700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 742 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 218 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 277 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 280 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.67 | g/cm³ | ASTM D 792 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+04 - 1.E+06 | Ohm-cm | ASTM D 257 |
| Source GMD, last updated:09/26/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 325 - 340 | °C |
| Front - Zone 3 Temperature | 325 - 340 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 315 - 325 | °C |
| Mold Temperature | 120 - 140 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/26/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton OX07411.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|