S-Plastics Valox EXVX1193resin is PET, Heat stabilized grade which can be used for FR Lampholder applications
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 230 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 230 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 280°C/2.16 kg | 30 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/25/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 90 - 120 | °C |
| Source GMD, last updated:08/25/2005 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1193.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|