S-Plastics Valox VX9520 resin is a flame retardant, 20% glass filled PET injection moulding resin with good color stability and good hearesistance.Applications: lamp socket
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 185 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1U |
| THERMAL | Value | Unit | Standard |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Ball Pressure Test, approximate maximum | 245 | °C | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 230 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.2 - 0.4 | % | S-Plastics Method |
| Density | 1.68 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 960°C, passes at | 1.6 | mm | IEC 60695-2-12 |
| Source GMD, last updated:11/14/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 90 - 120 | °C |
| Source GMD, last updated:11/14/2000 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox VX9520.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|