S-Plastics Valox VX8532 resin is a 30% glassfiber reinforced, non blooming, flame retardant PBT+PET blend with excellent surface appearance and good ultrasonic weldability properties.
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 45 | mg/1000cy | S-Plastics Method |
| Tensile Stress, break, 5 mm/min | 130 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 195 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9500 | MPa | ISO 178 |
| Hardness, H358/30 | 140 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.32 | W/m-°C | ISO 8302 |
| CTE, 23°C to 60°C, flow | 2.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.6 - 1 | % | S-Plastics Method |
| Density | 1.66 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.33 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 7 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.4 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0015 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.0131 | - | IEC 60250 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 31 | % | ISO 4589 |
| Source GMD, last updated:11/04/1998 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 285 | °C |
| Nozzle Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 255 - 280 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 110 | °C |
| Source GMD, last updated:11/04/1998 | ||
Other related products we recommend:
|