S-Plastics Valox VX4024 resin is 20% glass filled PBT.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7200 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 170 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 210 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.2 - 0.3 | % | S-Plastics Method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 15 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.6 | mm | UL 94 |
| Source GMD, last updated:06/10/1997 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:06/10/1997 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox VX4024.pdf |
|