S-Plastics Valox V9230 resin is a 15% glass reinforced PET injection moulding resin
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 135 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 230 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.7 - 1 | % | S-Plastics Method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| Source GMD, last updated:08/13/2002 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 35 - 65 | °C |
| Source GMD, last updated:08/13/2002 | ||
For more information please download the datasheet | |
 | S-Plastics Valox V9230.pdf |