S-Plastics Valox V4030 resin isGlass Filled Heat Stabilised PBT
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 100 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5600 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A |
| Volume Resistivity | 1.E+15 - 2.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | 1.E+15 - 2.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
| Source GMD, last updated:09/20/2007 | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 100 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5600 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.2 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index (UL) {PLC} | 1 | PLC Code | UL 746A |
| Volume Resistivity | 1.E+15 - 2.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | 1.E+15 - 2.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
| Source GMD, last updated:09/20/2007 | |||
|
For more information please download the datasheet |
|
 |