S-Plastics Valox EXVX1364 resin is 16% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 80 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 80 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.3 - 0.8 | % | S-Plastics Method |
| Density | 1.5 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 15 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:10/30/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 260 | °C |
| Nozzle Temperature | 230 - 255 | °C |
| Front - Zone 3 Temperature | 240 - 260 | °C |
| Middle - Zone 2 Temperature | 235 - 250 | °C |
| Rear - Zone 1 Temperature | 230 - 240 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:10/30/2008 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1364.pdf |
|