S-Plastics Valox EXVX1334 resin is 16% glass reinforced PBT+PET blend with improved surface appearance, UV stabilised
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 155 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5000 | MPa | ISO 178 |
| Hardness, H358/30 | 126 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 119 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 15 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 4.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 217 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 190 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 190 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.54 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.6 - 1 | % | S-Plastics Method |
| Density | 1.54 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.45 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 11 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, shorttime, 1.0mm | 21 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 0.8 mm | 25 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 |
| Relative Permittivity, 100 Hz | 3.5 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.2 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 100 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.001 | - | IEC 60250 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Comparative Tracking Index, M | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 27 | % | ISO 4589 |
| Source GMD, last updated:07/08/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 260 - 285 | °C |
| Nozzle Temperature | 265 - 275 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 255 - 280 | °C |
| Rear - Zone 1 Temperature | 240 - 260 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 60 - 110 | °C |
| Source GMD, last updated:07/08/2008 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1334.pdf |
|