S-Plastics Valox 315resin is Unreinforced, For extrusion/compounding only (not for injection molding). High viscosity. FDA and USP Class VI compliant. Melt viscositybetween 7500 and 9500 poise.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 300 | % | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 117 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Modified Gardner, 23°C | 40 | J | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 154 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 54 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C to 138°C, flow | 1.39E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Specific Volume | 0.76 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.08 | % | ASTM D 570 |
| Mold Shrinkage, flow, 0.75-2.3 mm | 0.9 - 1.6 | % | S-Plastics Method |
| Mold Shrinkage, flow, 2.3-4.6 mm | 1.5 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 1 - 1.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 2.3-4.6 mm | 1.6 - 2.4 | % | S-Plastics Method |
| Melt Viscosity | 700 | Pa-s | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >4.E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm | 15.7 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 23.2 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 3.3 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.1 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 |
| Source GMD, last updated:01/05/2000 | |||
| Parameter | ||
| Compounding Extrusion | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0 | % |
| Melt Temperature | 245 - 260 | °C |
| Barrel - Zone 1 Temperature | 200 - 230 | °C |
| Barrel - Zone 2 Temperature | 240 - 255 | °C |
| Barrel - Zone 3 Temperature | 240 - 275 | °C |
| Barrel - Zone 4 Temperature | 240 - 275 | °C |
| Adapter Temperature | 240 - 275 | °C |
| Die Temperature | 240 - 275 | °C |
| Waterbath Temperature | 25 - 35 | °C |
| Source GMD, last updated:01/05/2000 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox 315.pdf |
|