S-Plastics Thermocomp DF006LXN resin is a compound based on Polycarbonate resin containing Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 114 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 8630 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 149 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8230 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 114 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7.5 | % | ISO 527 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7860 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 914 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 144 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 144 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 140 | °C | ASTM D 648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 145 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.45 | - | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.07 | % | ASTM D 570 |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Source GMD, last updated:2010/07/09 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/07/09 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp DF006LXN.pdf |
|